Pierce height and pierce delay time is often overlooked, many operators are happy if the arc pierces the material and the cut begins successfully. The truth is that you can reduce frustration, reduce your cutting costs, and increase productivity by paying closer attention to your pierce settings, and it's really not difficult at all.
Piercing material is hard on the nozzle, much harder than just cutting, and the thicker the material is, the harder it will be on the nozzle. This is because thicker material takes longer to pierce, and because more molten metal will be ejected upwards toward your torch prior to blowing a hole through the bottom. Shops that cut a lot of thick plate will often use chain cutting, or edge starts to eliminate the number of pierces, but with metal art you typically can't escape high pierce counts.
We have established that even a perfect pierce will be hard on the nozzle, but an imperfect pierce could destroy a brand-new nozzle before you even cut 1 inch of material. This is a common source of frustration for many new operators. The most common mistake when piercing is being too close to the material or in contact with the material. You can't trust that you are at the correct pierce height just because you have the proper height set in your software, you must stop and measure your pierce height to be sure it is correct. The best way to measure pierce height is to run your program and pause the machine after the initial height sensing is complete, and the torch has raised to the pierce height set in your software. Use a set of feeler gauges to determine what the height is. The correct height can be found in the cut charts for your plasma cutter, or a good rule of thumb is 1.5-2 times the cut height.
If your cut height is too low, the most common reason is that the material has flexed down during the initial height sensing and flexed back up when the torch lifted off to the pierce height. The only accurate way to resolve this issue is to hold the material down during the initial height sensing. If material flex is not your issue, it could be that your Z axis is not accurately calibrated, or you could simply have wear and slop in your z axis. Either of these 2 can be resolved by "fudging" the pierce height setting in your software to achieve the correct height. Piercing too high is not as common and can be almost as damaging, but easily corrected by adjusting the pierce height setting in your software.
Once you have your pierce height working perfect, it is time to move on to the pierce delay time, which is typically measured in milliseconds (ms). The correct length of time for the material thickness you are cutting can be found in the cut charts for your plasma cutter, the thicker the material is, the longer it will take to pierce. If cut charts are not available for your plasma cutter, the general rule of thumb is to use the shortest length of time possible. The moment the arc pierces through the material, you want your XY motion to begin. If it is left to pierce for too long, the plasma arc will wander to maintain its transfer to ground, and this will damage your nozzle quickly. If your pierce time is too short, a small section of your part may remain uncut at the beginning.
It is common for operators to disregard things like piercing because it seems so simple and unimportant in the big picture, but it is very important and I hope this helps some operators to improve their performance and consumable life.
Keep cutting and have fun
Piercing Height & Pierce Delay Time - Very Important
Important information to prevent common issues faced by many getting started in cnc plasma cutting.
-
- 2 Star Member
- Posts: 76
- Joined: Tue Jul 22, 2008 3:26 pm
Return to “CNC Plasma Beginners Knowledge Base”
Jump to
- WELCOME CENTER, GOOD INFO & MEET OUR SPONSORS
- ↳ Introduce Yourself
- ↳ CNC Plasma Beginners Knowledge Base
- ↳ Contributing Membership Registration or Renewal
- ↳ Our Sponsors & Advertisers
- DXF DESIGN & PROJECT PICTURE SHARING FORUMS
- ↳ DXF & SVG Plasma Cutting File Sharing Forum
- ↳ CNC Plasma Cutter Project Picture Gallery
- ↳ File Conversion Help Wanted
- ↳ Categorized DXF & SVG Library
- GENERAL FORUMS
- ↳ CNC Plasma Cutters General Forum
- ↳ Plasma Cut Quality Forum
- ↳ Hypertherm's Basic Tips to Improve Cut Quality
- ↳ Hypertherm's 10 Common Plasma Cutting Mistakes
- ↳ Hypertherm's Tips to Troubleshoot Cut Angularity
- ↳ Pricing, Advertising, & Marketing Your Products Forum
- ↳ Tech Tips From Other Members
- ↳ Classified Ads
- PLASMA CUTTER FORUMS
- ↳ Hypertherm Plasma Cutters
- ↳ Powermax Helpful Resources
- ↳ Powermax Cut Speed Charts
- ↳ Powermax Cut Speed Charts
- ↳ Powermax SYNC 65, 85, 105 Cut Speed Charts
- ↳ Powermax 45 Cut Speed Charts
- ↳ Powermax 65/85 Cut Speed Charts
- ↳ Powermax 105 Cut Speed Charts
- ↳ Powermax 125 Cut Speed Charts
- ↳ Powermax Fault Code, Diagnostics, & Troubleshooting Forums
- ↳ Powermax 65 & 85 Common Fault Code, Diagnotics, & Troubleshooting Forum
- ↳ 0-12 Fault Code
- ↳ 0-19 Fault Code
- ↳ 0-20 Fault Code
- ↳ 0-21 Fault Code
- ↳ 0-22 Fault Code
- ↳ 0-30 Fault Code
- ↳ 0-99 fault Code
- ↳ Displaying the Powermax 65 85 Service Screen
- ↳ Thermal Dynamics / Esab Plasma Cutters
- ↳ Cutmaster A40 Cut Speed Charts
- ↳ Cutmaster A60 Cut Speed Charts
- ↳ Cutmaster A80 Cut Speed Charts
- ↳ Cutmaster A120 Cut Speed Charts
- ↳ Lincoln & Miller Plasma Cutters
- ↳ RazorWeld, Everlast, & All Other Plasma Cutters
- ↳ Plasma Consumables
- CNC PLASMA TABLE & CONTROLLER FORUMS
- ↳ CandCNC Forum
- ↳ CandCNC Website
- ↳ FastCut CNC Forum
- ↳ FlashCut CNC Forum
- ↳ JD Squared Forum
- ↳ JD Squared Website
- ↳ Shop Sabre Forum
- ↳ Star-Lab CNC Forum
- ↳ Tracker CNC Forum
- ↳ Langmuir Crossfire Forum
- ↳ PlasmaCam, Samson, & Go Torch Forum
- ↳ Torchmate Forum
- ↳ DIY Plasma Table & Accessory Discussion Forum
- ↳ Various Manufacturers Forum
- CAD-CAM & CONTROL SOFTWARE FORUMS
- ↳ General Discussion
- ↳ Fusion 360 & AutoCAD Forum
- ↳ Get AutoDesk Fusion 360 FREE
- ↳ BobCAD
- ↳ C&CNC CommandCNC
- ↳ Corel Draw Graphics Suite
- ↳ CorelDRAW Free 30 day trial
- ↳ Quick & Helpful CorelDRAW Tutorial Videos
- ↳ Inkscape
- ↳ Download Inkscape for Windows
- ↳ Linux CNC - Plasmac
- ↳ Mach3 & Mach4 CNC
- ↳ Plasmacam - DesignEdge
- ↳ SheetCam
- ↳ Torchmate Software
- METAL FINISHING FORUMS
- ↳ Patina Finishes
- ↳ Steel F/X Your Metal Patina & Dye Connection
- ↳ Paint & Other Top Coats
- ↳ Powder Coat
- ↳ Abrasive & Texturing
- ↳ Dross/Slag Removal
- ACCESSORIES & RELATED TOOL FORUMS
- ↳ EasyScriber Drag Style Scriber for Hypertherm
- ↳ EasyScriber for Hypertherm, Thermal Dynamics, Razorweld, Esab
- ↳ Plate Markers, & Air Scribes
- ↳ Mig Welders, Tig Welders, Spot Welders
- ↳ Metal Bending, Rolling, Notching, Drilling, Saw Cutting
- ↳ Air Dryers, Air Filters, Air Compressors, Etc.
- ↳ Water Tables, Ventilation, Air Handling
- ↳ Fab Tables, Grind Stations, Material Storage & Handling
- ↳ Pen Markers, Remote Controls, Drawing Tablets, etc.
- ↳ 3D Printers & Printed Accessories
- ↳ Laser Engravers & Cutters
- ↳ Arclight Dynamics